Resin sculpture mold silica gel is mainly used for compounding large, medium and small pieces of resin model craft pendants, handicraft sculptures, animal clay molds, fine glass fiber reinforced plastic sculptures, character sculptures, animation game character models, traditional plaster statues, Guanyin plaster statue molds, clay sculptures Models, animal clay sculpture molds, glass fiber reinforced plastic sculptures.

SKU: PSD001-HY635 分类:

描述

Basic introduction of resin sculpture mold silicone:

Resin sculpture mold silicone contains two types: condensation mold silicone and addition mold silicone. The former is a traditional industrial-grade silicone with a ratio of 100:5, and the latter is a popular addition-molding silicone in recent years, also called food-grade silicone. , Environmentally friendly, non-toxic and tasteless, there are two ratios of 1:1 and 10:1, 1:1 silica gel is used more.

For the production of resin sculpture molds, brush mold silica gel is used more, mainly because resin sculpture products are generally large in size, and the pattern is very fine, and the texture is particularly complex. Using brush mold silica gel can better complicate the product. Copy the context;

For some resin sculpture products with relatively simple patterns, it would be better to use molded silica gel. Firstly, the product lines can be better replicated, secondly, it can save operation time, and thirdly, it can also save labor costs.

Therefore, you can select the appropriate resin sculpture mold silicone according to the actual situation of your product.

Uses of resin sculpture mold silicone:

Resin sculpture mold silicone is mainly used for various large, medium and small pieces of resin model craft pendants, handicraft sculptures, animal clay sculpture molds, fine glass fiber reinforced plastic sculptures, character sculptures, animation game character models, traditional plaster statues, Guanyin plaster statue molds, clay sculptures Models, animal clay plastic molds, glass fiber reinforced plastic sculptures, government building models and other products made of silicone molds. It is also often used in the manufacture of molds for fine products such as film and television prop models, car models, and military gift models.

Application characteristics of resin sculpture mold glue:

①It has excellent burning resistance. The high temperature resistance can generally reach 180℃-250℃. With special materials, it can reach 300℃, which can effectively solve the problem of resin products that burn out the silicone mold due to heat during the curing process;

②It does not emit oil, it is the leader in the colleague silica gel. It solves the problem of oil emission that often occurs in the process of reversing the resin product of the silicone mold and prolongs the service life of the silicone;

③The hardness, viscosity, and operating time of the silicone can be produced according to customer needs, and the production of silicone can be tailored for you;

④The shrinkage rate is smaller than that of its peers, the silicone molds made are more durable, and the number of mold turns is high, which effectively saves production costs;

⑤The tear resistance and stretching ability are good, and the made silicone mold is more durable and does not deform;

 

Instructions for use of resin sculpture mold silicone:

According to the different operation methods, there are three mold opening methods: wrap mold, brush mold (split mold, three-dimensional mold, plane mold), and perfusion mold.

Reference to the reaction situation of the ratio of silica gel and curing agent:

1. When the amount of curing agent is 1%, the colloid will still flow in 2.5 hours, and it can be demoulded in 6-8 hours.

2. When the amount of curing agent is 2%, the colloid will still flow in 50 minutes to 1 hour, and it can be demoulded in 2-3 hours.

3. When the amount of curing agent is 3%, the colloid will still flow in 28-30 minutes, and it can be demoulded in 1.5-2 hours.

4. When the amount of curing agent is 4%, the colloid will still flow in 10-15 minutes, and the mold can be demolded in 1 to 1.5 hours.

Resin sculpture mold silicone-HY635

其他信息

Type

HY-635

Viscosity(mPa.s)

27000±8000

Hardness(Ao)

25±2

Tensile Strength(Mpa)

9

Tensile tear strength(KN/m)

35

Elongation(%)

420

Curing agent addition ratio(%)

2~5

Operating time(h)

0.5-1

Curing time(h)

3-4